2D SiC fiber-SiC (SiC/SiC) composites were fabricated via slurry infiltration and a stacking process. The effects of the additive composition and content in SiC slurries and the effect of the sintering time on the sintered density and strength of SiC/SiC composites were investigated. A slurry containing $Al_2O_3-Y_2O_3-MgO$ (AYM) additives led to a higher strength compared to a slurry containing $Al_2O_3-Y_2O_3-CaO$ (AYC) additives. The sintered density increased as the sintering time increased and showed a maximum (>98%) at 4 h. In contrast, the flexural strength increased as the sintering time increased and showed a maximum (615 MPa) at 6 h. The relative density and flexural strength increased as the additive content increased.