In this study we investigated the variation of the substrate temperatures using RF sputtering to identify the effect on the structure and electrical properties by c-axis orientation of ZnO thin film. ZnO thin films were prepared on Al/Si substrate. In our experimental results, ZnO thin film at $300^{circ}C$ was well grown with (002) peak of ZnO thin film, the thin film showed the high resistivity with the value of $5.9{ imes}10^7;{Omega}cm$ and the roughness with 27.06 nm. As increased the substrate temperatures, the grain size of ZnO thin films was increased. From these results, we could confirm the suitable substrate temperature of ZnO thin films for FBAR(film bulk acoustic resonator).