This paper investigated how Fine Fly Ash (FFA) with $14,000;cm^2/g$ of Fineness affects the micro structure and material properties of High-Performance Concrete (HPC) before and after hardening from Material Test of HPC and Cement Paste. FFA is applied as a substitute of Silica Fume which is used necessarily in producing HPC. As a Material Test results, 5% FFA series specimen shows the lower fluidity than SF series specimen. When, however, the Fluidity of 10% FFA series specimen is increased reversely to the similar value of SF series specimen. The Porosity of FFA series specimen of 3 day age is displayed to $21{sim}24%$, which is higher than $19{sim}20%$ porosity of SF series specimen, while that of 28 day age is reached to $8{sim}9%$, which is improved compared with 10% fo SF series specimen. It can be thought that FFA has better influence on the porosity of HPC in case of long term age. The Compressive strength of FFA series specimen shows the similar result with the property of porosity. The compressive strength of 28 day age FFA series specimen is $98{sim}106%$ of SF series specimen and 107% of plain specimen to reveal better strength development.