Investigation of improving the properties of UV detector which uses the wide bandgap of ZnO are under active progress. The present study focused on the design and fabrication of i-ZnO/p-inversion $layer/n^--Si$ Epi. which is characterized with very thin p-type inversion layer for UV detectors. The i-ZnO thin film for achieving p-inversion layer which was grown by RF sputtering at $450^{circ}C$ and then annealed at $400^{circ}C$ in $O_2$ gas for 20 min shows good intrinsic properties. High (0002) peak intensity of the i-ZnO film is shown on XRD spectrum and it is confirmed by XPS analysis that the ratio of Zn : O of the i-ZnO film is nearly 1 : 1. Measurement shows high transmission of 79.5 % in UV range (< 400 nm) for the i-ZnO film. Measurement of $V_r-I_{ph}$ shows high UV photo-current of 1.2 mA under the reverse bias of 30 V.