The effect of CaO mold on the formation of reaction layer was investigated. CaO mold was prepared by mixing of Colloidal silica($NALCO^{(R)}$ 1130) and an $ZrO_2$, CaO at room temperature. The dried at $20{pm}3^{circ}C$, 75% humidity for 12hrs. Sample was prepared from the Cp-Ti(grade-2) and melted by high frequence induction melting system in the vacuum condition. The react ion layer of Ti was confirmed by optical microscopy, microhardness(Hv) and X-ray diffraction. Thickness of reaction layer using the CaO stabilized ZrO2 was thinner than the CaO added ZrO2. And thickness of reaction layer were decreased with decreasing pH of slurry. CaO addition in the slurry could not controlled reaction between molten Ti and investment mold. On the other hand, the CaO chemical bonded ZrO2 by stabilization treatment could controlled reaction between molten Ti and investment mold.