Methyl methacrylate(MMA) was grafted onto microcrystalline cellulose(MCC) with ceric ammonium nitrate(CAN) as a redox initiator at the various conditions. The cellulose triacetate(CTA) composite films added MCC and MMA-grafted MCC powders were prepared on a glass plate. The graft yield(GY) and graft efficiency(GE) of the grafted MCC were calculated with the simple equations by the weight balance method. The double bond of C=O on the grafted MCC surfaces was confirmed by the fourier transform infrared spectroscopy with attenuated total reflection(FT-IT ATR) spectrophotometer. After grafting, the degree of crystallinity of cellulose powders was decresed by judging from x-ray diffraction(XRD) data. Scanning electron microscope(SEM) photos showed the only solvent and CAN solution could change the roughness of MCC powders and the effect of powder dispersions in composite matrix. The tensile strength of MCC/CTA composite films was decreased with increase of MCC powder contents. When 5% grafted MCC was added, the tensile strength of grafted MCC/CTA composite films was increased from 82.3 MPa to 97.2 MPa. The thermal property of powders was also analyzed by the thermogravimetric analysis(TGA).