Epoxy/Organically Modified Layered Silicate Nanocomposites were prepared by dispersing synthetic layered silicate modified with alkyl ammonium ions. In the dispersing process, the organically modified layered silicate were mixed in epoxy resin with shearing, and aggregation of the silicate were removed by centrifugal separation after mixing epoxy resin and silicates. Micrographs taken by transmission electron microscopy(TEM) indicate that the nanocomposites have a mixed morphology including both parallel silicate layers and exfoliated silicate layers area, As the thermal properties, the glass transition temperature of the nanocomposites was shifted to a higher temperature($+6^{circ}C$)than pure epoxy. Furthermore, dispersion of OMLS will prevented relative permittivity from increasing at a high temperature above the glass transition temperature.