Alumium alloys hot forging process are gaining increased acceptance in the automotive and electronic industries and hot forging is one of the most efficient manufacturing method for mass product parts. It has been investigated the microstructures and mechanical properties of Al-11.7Si-0.5Mg (KNT40-T6)alloy fabricated by hot forging process for development of connecting rod in this study. The microstructure of hot forged specimen was composed of eutectic structure of alumimum solid solution and $Mg_2Si$ precipitates. The tensile strength of solutionized Al-11.7Si-0.5Mg alloy was 217MPa. This alloy showed a good corrosion resistance using electrochemical polarization test.