Field emitter arrays (FEAs) were developed using carbon nanotubes (CNTs) as electron emission sources. The CNTs were grown using a selective-positioning technique with a resist-protection layer. The light emission properties were studied through the electron emission of the CNTs on patterned islands, which were modulated with island diameter and spacing. The electron emission of CNT arrays with $5{mu}m$ diameters and $10{mu}m$ heights increased with increased spacing (from $10{mu}m$ to $40{mu}m$). The electron emission current of the $40-{mu}m$-island-spacing sample showed a current density of 1.33 mA/$cm^2$ at E = 11 V/${mu}m$, and a turn-on field of 7 V/${mu}m$ at $1{mu}A$ emission current. Uniform electron emission current and light emission were achieved with $40{mu}m$ island spacing and $5{mu}m$ island diameter.