A simple strategy was developed based on polyelectrolyte/silver nanocomposite to obtain humidity-sensitive membranes. The major component of a humid membrane is the polyTEAMPS/silver nanocomposite obtained by thermal heating the mixture of a polyelectrolyte and silver isopropylcarbamate complex. Humidity sensors prepared from polyTEAMPS/silver (w/w=100/0 and 100/6) nanocomposites had an average impedance of 292, 8.83 and $0.86;k{Omega}$, and 5,327, 140 and $0.93;k{Omega}$ at 30,60 and 95% relative humidity (RH), respectively. Hysteresis, temperature dependence and response time were also measured. Activation energies and complex impedance spectroscopy of the various components of the polyelectrolyte/silver nanocomposite films were examined for the humidity-sensing membrane.