[ $TiO_2-V_2O_5$ ] sol was fabricated using sol-gel method and $TiO_2-V_2O_5$ thin films were fabricated using dip-coating method. $V_2O_5$ sol was added 0.01mole, 0.03mole, 0.05mole into $TiO_2$ sol. As a results of crystalline properties, $V_2O_5$ peaks were not found in spite of $V_2O_5$ additive. Thickness of thin films increased $0.1{sim}0.25{mu}m$ every a dipping. Capacitance of thin films increased with increasing heat treatment temperature and it increased largest at $700^{circ}C$. Capacitance of thin films decreased with increasing $V_2O_5$ additive and it increased largest at 0.01mole. Because adsorption time and desorption time of thin films was about 2 minutes 40 seconds and about 3 minutes 40 seconds respectively, adsorption time was faster about 1 minutes than desorption time.