We have examined the effect of ball-milling on the superconducting properties of $MgB_2$ doped with C. The ball-milling of pre-reacted $MgB_2$ powder was carried out in dry or wet state using C or diethylenetriamine ($C_{4}H_{13}N_3$) as additives. The diethylenetriamine, whose chemical formula contains no oxygen, was chosen to avoid an excess oxidation during doping. The superconducting transition temperature (Tc) of the ball-milled or doped $MgB_2$ powders was only slightly smaller than that of undoped $MgB_2$. The critical current density (Jc) of the highly ball-milled $MgB_2$ was higher than that of C-doped $MgB_2$. The addition of diethylenetriamine was detrimental to Jc, although Tc was almost unchanged.