In-plane shear tests were performed to investigate the shear property change of FRP by plasma modification. Graphite/epoxy prepreg was used as a test material and plasma source was a microwave (2.4GHz) type. Plasma was induced by oxygen gas and its flow rate was kept $4{sim}5$sccm with low vacuum state of $10^{-3}$ Torr. Prepreg was stacked unidirectionally ($[0^0]_8$) after plasma modification. Wettability was determined by measuring a contact angle. The results showed that the contact angle was decreased from $86^0$ to $45^0$ after plasma modification. Shear strength was also improved by ${sim}10%$. SEM examination was made on the fracture surface and functional group produced by the plasma modification was investigated by XPS.