The microwave dielectric properties of $LiNb_3O_8-TiO_2$ based ceramics with low firing agents, CuO, $Bi_2O_3$, $B_2O_3$, $SiO_2$, $TiO_2$, were investigated to improve the sintering condition for the LTCC system. According to the X-ray diffraction and SEM, the ceramics of $LiNb_3O_8-TiO_2$ with low firing agents showed no significant second phases within a range of experiments, and fine microstructures. By adding the low firing agents, the sintering temperature decreased from $1200^{circ}C$ to $925^{circ}C$. Based on the results of electrical measurements, the $LiNb_3O_8-TiO_2$ ceramics showed a promising microwave dielectric properties for LTCC applications, those are ${varepsilon}_r$ (dielectric constant) = 44, Q f (quality factor) = 18000, and ${ au}_f$ (the temperature coefficient of resonant frequency) = $-1.5;ppm/^{circ}C$.