Porous SiC candle filter preforms were fabricated by extrusion and ramming process. To fabricate SiC candle filter preform, commercially available 85 ${mu}m;{alpha}-$-SiC powder and 44 ${mu}m$ mullite, CaC$O_3$ powder were used as the starting materials. The candle type preforms were fabricated by vacuum extrusion and ramming process, and sintered at $1400{^{circ}C}$ 2 h in air atmosphere. The effect of forming method on porosity, density, strength (flexural and compressive strength) and microstructure was investigated. Also, corrosion test of the sintered candle filter specimens as forming method was performed at $600{^{circ}C}$ in IGCC syngas atmosphere. The sintered SiC filter which was formed by ramming process has more higher density and exhibit higher strength than extruded filter. Its maximum density and 3-point bending strength were 2.00 g/$cm^3$ and 45 MPa, respectively.