The present works were performed that titanium foil was anodized in various dilution ratios of seawater and distilled water with 10V external voltage applied, then annealed at $450^{circ}C$ to obtain $TiO_2$ on the Ti substrate. The prepared samples were characterized by instruments (XRD, SEM, and photocurrent) and used to investigate rate of hydrogen production in photoelectrochemical cell as well as Cr(VI) reduction. As the results of experiments, the anodized $TiO_2$ in seawater electrolytes, which are ranged from 15 to 50 times dilution of seawater, was showed a relatively higher hydrogen production (ca. 97~110 umol/hr-$cm^2$) and Cr(VI) reduction (ca. 95% reduction).