In order to investigate the microstructural morphology of the sulfide expected from the Fe-FeS phase diagram, a vacuum-sealed quartz tube where pure iron (99.9%) and sulfur (99.99%) powders were charged was heated upto $1000^{circ}C$ in the electric resistance furnace, held for 96 hours and quenched in cold water and then, rod specimen was produced. Compositional difference of the sulfur between upper and lower parts of the rod was 7.5wt.% and segregation of the sulfur was gradually increased from the lower part to the upper one of the rod. The rod specimen was divided into three parts by the microstructural morphology of the sulfide. The upper part of the rod specimen revealed single phase FeS intermetallic. In the middle part of the specimen, hyper-eutectic microstructure where primary FeS was precipitated first and then, eutectic of $alpha$-Fe and FeS was formed in the inter-dendritic region of the FeS. Especially, hypo-eutectic microstructure was appeared in the lower part of the specimen. After primary dendrite of $alpha$-Fe solidified, FeS dendrite which included small amount of $alpha$-Fe and FeS eutectic in the inter-dendritic region was formed.