Sulfide stress corrosion cracking (SSCC) in crude oil field environment containing hydrogen sulfide (H2S) has been recognized as a material degradation and damage mechanism. Laboratory data and field experience have demonstrated that extremely low concentration of H2S may be sufficient to lead to SSCC failure of susceptible materials. In some cases, sulfides may act synergistically with chlorides to produce SSCC failures. SSCC mechanism is a form of hydrogen embrittlement that occurs in high strength steels and in localized hard zones in weld of susceptible materials. In the heat-affected zones adjacent to the weld, there are often very narrow hard zones combined with regions of high residual stress that may become embrittled to such an extent by dissolved atomic hydrogen. On the basis of this understanding, SSCC tests were conducted with smooth specimens of the multi-pass welded ASTM A106 Gr B steel pipe used in the oil industries. And SSCC resistance according to the welding processes was evaluated. From the results, the weld by GTAW+FCAW showed the largest resistance against SSCC.