Purpose: Platelet derived growth factor(PDGF)-BB and bone morphogenetic protein(BMP)-2 are well-known representative growth factors. The purposes of this study were to investigate the effect of rhPDGFBB and rhBMP-2 on osseointegration of titanium implants at periimplant bone defects grafted with hydroxyapatite and to evaluate the feasibility of imaging bone structures around screw-type titanium implant with micro-CT. Materials and Methods: The first molar and all premolars in the mandible region of four beagle dogs were extracted. Following a healing period of 4 months, three $8{ imes}8{ imes}6mm$-sized bony defects were formed and screw-type titanium implants were placed with hydroxyapatite(HA) block and growth factors; Control group, PDGF group and BMP group. Two months post-implantation, the mandible was harvested. Bone volume(BV), bone-to-implant contact(BIC) and bone mineral density(BMD) were analyzed with micro-CT and histology. Results: According to micro-CT analysis, BV and BMD measures of PDGF and BMP group were significantly higher than control group(BV; PDGF group: $p{fallingdotseq}0.011$, BMP group: $p{fallingdotseq}0.006$/BMD; PDGF group: $p{fallingdotseq}0.020$, BMP group: $p{fallingdotseq}0.011$) and BIC measures of BMP group were significantly higher than PDGF group($p{fallingdotseq}0.015$). In histologic evaluation, BIC measures of BMP group was significantly higher than PDGF group($p{fallingdotseq}0.048$). The values of BV in histologic sections were higher than in micro-CT images and the values of BIC in micro-CT images were higher than in histologic sections. Conclusion: The findings of this experimental study indicates that the use of rhPDGF-BB and rhBMP-2 can increase new bone formation in a large bony defect around titanium implant, and rhBMP-2 is more effective than rhPDGF-BB. Micro-CT can be considered useful for assessment as a rapid and nondestructive method for 3-dimensional measurement of bone healing around implants. Further study is necessary, however, to remove metal artifacts around titanium implant and to standardize the method.