We fabricated nano-templates by low temperature BCP(block copolymer) process at 180 $^{circ}C$, then we deposited 10 nm-thick $TiO_2$ layers with ALD(atomic layer deposition) at low temperature of 150 $^{circ}C$. Through FE-SEM analysis, we confirmed the successful formation of the groove-type(width of crest : 30 nm, width of trough : 18 nm) and the cylinder-type(diameter : 10 nm, distance between hole : 25 nm) templates. Moreover, after $TiO_2$-ALD processing, we confirmed the deposition of the uniform nano layers of $TiO_2$ on the nano-templates. Through AFM analysis, the pitches of the crest-through(in groove-type) and hole-hole(in cylinder-type) were the same before and after $TiO_2$-ALD processing. In addition, we indirectly determined the existence of the uniform $TiO_2$ layers on nano-templates as the surface roughness decreased drastically. We successfully fabricated nano-template at low temperature and confirmed that the three-dimensional nano-structure for sensor application could be achieved by $TiO_2$-ALD processing at extremely low temperature of 150 $^{circ}C$.