Phase stabilized leucite, which has high coefficient of thermal expansion, was synthesized, and its thermal expansion behavior was investigated. The homogeneous leucite phase was synthesized by solid state reaction from the mixture of $K_2CO_3-Al_2O_3-SiO_2$. and its stabilization from tetragonal to cubic phase was attempted by adding $Cs_2CO_3$ into starting materials. And fine powder with an average particle size of a few hundreds ${mu}m$ were fabricated by planetary milling. During milling, amorphization of leucite was observed and recrystallized after heat treatment. The thermal expansion behavior of tetragonal and cubic leucite has measured and discussed. The average coefficient of thermal expansion of tetragonal and cubic phase leucite from room temperature to $750^{circ}C$ was $21.4{ imes}10^{-6}/^{circ}C$ and $14.5{ imes}10^{-6}/^{circ}C$, respectively.