In this work, the scintillation properties of CsI:Na crystal were investigated as radiation detection sensor. This scintillation material was grown by a 2-zone vertical Bridgman method. Under X-ray excitation the crystal shows a broad emission band between 280 nm and 690 nm wavelength range, peaking at 413 nm. Energy resolution for $^{137}Cs$ 662 keV $gamma$-rays of the crystal was measured to be 6.9 %(FWHM). At room temperature, the crystal exhibits three exponential decay time components. The fast and major component of scintillation time profile of the crystal emission decays with a 457 ns time constant. Absolute light yield of the crystal was estimated to be 53,000 ph/MeV using LAAPD. The sample crystal shows proportionality of 30 % in the measured energy range from 31 to 1,333 keV. And the $alpha/eta$ ratio of the crystal was 0.14.