Poly (N,N-dimethylacrylamide) is very useful in various fields due to its remarkable properties, such as water solubility and biocompatibility. This study used N,N-dimethylacrylamide with the cross-linker EGDMA (ethylene glycol dimethacrylate), HEMA (2-hydroxyethyl methacrylate), MMA (methyl methacrylate), NVP (N-vinyl-2-pyrrolidone) and the initiator AIBN (azobisisobutyronitrile) for copolymerization. Measurement of the physical properties of the copolymerized polymer showed that the water content was 36 - 42%, refractive index was 1.433 - 1.426 and visible ray transmittance 90 - 91% while the oxygen permeability showed a distribution between 13.1 and $21.29{ imes}10^{-11}(cm^2/sec)$ ($mlO_2/mL{ imes}mmHg$). The measurement showed that the increased amount of oxygen permeability of the copolymer measured using the polarographic method range between 11.0% and 80.5%. Based on the results of this study, the produced copolymer is suitable for use as a material to high oxygen permeability hydrogel lenses.