We report the effect of surface morphology on the conductivity of the poly-N-vinylcarbazole (PVK)/silica gel ($SiO_2$) nanocomposites as a function of $SiO_2$ weight percentage (%).The polymerization of PVK was initiated by a free-radical polymerization. The surface morphology of the prepared composite shows the incorporation of $SiO_2$ in the prepared PVK-$SiO_2$ (PS) nanocomposites. The conductivity increased from $9.2{ imes}10^{-5}S;cm^{-1}$ to $9.6{ imes}10^{-4}S;cm^{-1}$ with the increase in the percentage of silica gel from 5 to 30%. The nanocomposites show a percolation behavior having a threshold value between 15 and 20%.