$SnO_2-(1-x)P_2O_5-xB_2O_3$ glass system were prepared by melt-quenching technique in the compositional series containing 50, 55 and 60 mol% of $SnO_2$. Local structure of the glasses was investigated by Raman and FT-IR measurements. A large glass-forming region was found at the phosphate side of the ternary system with homogeneous glasses containing up to 5~25 mol% of $B_2O_3$. According as content of $B_2O_3$ increases, theraml expansion coefficient of glass decreased but transition temperature and softening temperature increased. Because these phenomenon changed local structure of glass. According as content of $B_2O_3$ increases, quantity of bridging oxygen increased. Also, according as content of $SnO_2$ increases, confirmed that quantity of non-bridging oxygen increases.