In the present work, the influence of oxide on the Cr-Si-N coatings was investigated for the Cr-Si-O-N coatings on AISI 304 and Si wafer deposited by hybrid system, which combines the DC magnetron sputtering technique and arc ion plating (AIP) using Cr and Si target in an $Ar/N_2/O_2$ gaseous mixture. As the O content in the Cr-Si-N coatings increased, the diffraction patterns of the Cr-Si-O-N coatings showed CrN and $Cr_2O_3$ phases. However, as the O content increased to 28.8 at.%, diffraction peak of $Cr_2O_3$ was disappeared in the Cr-Si-O-N coating. The $d_{200}$ value was decreased with increasing of O content. The average grain size increased from about 40 nm to 65 nm as the O content increased. The maximum micro-hardness of the Cr-Si-O-N coating was obtained 4507 Hk at the O content of 24.8 at.%. The average friction coefficient of the Cr-Si-O-N coatings was gradually decreased by increasing the O content and the average friction coefficient decreased from 0.37 to 0.25 by increasing the O content. These results indicated that amorphous phase was increased in the Cr-Si-O-N coatings by increasing of O content.