In this work we synthesized both MgB2 and Carbon doped MgB2 superconductor with Ag addition via high energy milling and substituent heat treatment. Heat treatments were performed at $900;^{circ}C$ for 30 min in flowing Ar gas. We varied amount of Ag powder. In a range of Ag powder was 0~5wt%. The effect of Ag was correlated with superconducting properties. The results show a slight decrease in critical temperature ($T_c$) and a reduction of critical current density ($J_c$) at high fields for the Ag-doped samples as compared to the un-doped samples. Reduction of $J_c$ may be due to the formation of MgAg compound.