In this study, the performance improvement of epoxy resin system had been tried by the improvement of particle size distribution and globularization of filler using polymerization method. From the results of particle size distribution measurement, the polydispersity value of reformed filler was 1.04 and that of silica flour before reformation was 2.6, it could be confirmed that the particle size uniformity of reformed filler had been improved greatly and the shape of particle was globular. Compatibility between monomer and silica was improved remarkably with the silanization pretreatment of silica flour. From the results of degree of crosslinking test, it could be confirmed that the binding structure of reformed filler was 3-dimensional net structure. And it could be also confirmed that the fluidness was improved at the casting of epoxy resin with reformed filler. From the above results, it could be concluded that the reformation of filler with the improvement of particle size distribution and globularization was very successful method to improve the performance of cast epoxy resin system.