A series of fatigue tests have been performed on the non-load carrying fillet welded joints in order to quantitatively assess the fatigue characteristics due to the grindings and TIG(Tungsten Inert Gas) welding treatments. From the results of fatigue tests, it has been shown that the fatigue strengths at $2{ imes}106$ load cycles were improved in the case of the grinding sand TIG welding treatments, and we could know that it is satisfying fatigue strength prescribed in fatigue design standard in general. Besides, from the results of fracture mechanics approaches, the geometric shape correction factors were the most dominant factors in the initial fatigue crack growth, but as the fatigue crack develops, the finite plate correction factor were became the most dominant factor, and the fatigue life on non-load carrying fillet welded joints could be relatively exactly estimated by using the relations between fatigue crack growth rate and stress intensity factor obtained from finite element analysis and existing proposed formulae.