Regenerated cellulose was prepared from Buckeye wood pulp V60 via dissolution in N-methylmorpholin N-oxide (NMMO) solvent system. The effect of antioxidants such as, n-propylgallate (PG), tris(nonylphenyl) phosphite (TRIS), ethylenediamine tetraacetic acid disodium salt (EDTA), and magnesium sulfate on the properties of regenerated cellulose was studied using X-ray diffraction, copper index calculation, and viscometry. Only addition of more than 0.01% of PG into NMMO solvent was effective to avoid the reduction of the degree of polymerization(DP) of regenerated cellulose during dissolution at $110^{circ}C$. However, the early stage(within 0.5h of dissolution process) degradation of cellulose was not prevented eventhough up to 0.5% PG was appled to hot NMMO system. In addition, to recover the expensive NMMO after cellulose regenerating process, the washing filtrate was studied using simple techniques, such as refractive index, pH, and conductivity measurements. Through conductivity measurement result, 4-time of washing was enough to remove the NMMO completely from regenerated cellulose.