The evolution of microstructure and phases of Mg-10Al-Mn alloy by cooling plate method during homogenization treatment have been investigated with metallographic analysis, scanning electron microscopy and energy dispersive spectroscopy. The ingots used for this experiment were prepared by cooling plate and homogenization heat treatment was performed at 300 and $400^{circ}C$ for various holding times (0, 1, 4, 8 and 12h). The casting ingots were consisted of the fine grains and eutectic phases. And, these eutectic phases were dissolved into the matrix during homogenization treatment at $400^{circ}C$ but the lower temperature (at $300^{circ}C$) did not be.