0.96$(Na_{0.5}K_{0.5})NbO_3$-0.04$(Ba_{(1-x)}Sr_x)TiO_3$ lead free piezoelectric ceramics were synthesized to enhance the piezoelectric properties of (Na,K)$NbO_3$. The systhesis and sintering method were the conventional solid state reaction method and general sintering method in air atmosphere. The polymorphic phase transition(PPT) was observed at all composition(0 $leq$ x $leq$ 0.05) when $(Ba_{(1-x)}Sr_x)TiO_3$ were added in the $(Na_{0.5}K_{0.5})NbO_3$. As Sr concentration was increased, grain size, dielectric loss(tan$delta$) and mechanical quality factor($Q_m$) were decreased and piezoelectric constant($d_{33}$) and electromechanical coupling factor($k_p$) were increased within a limited value. The optimized piezoelectric and properties, $d_{33}$, $k_p$, $Q_m$, and tand, of 0.96$(Na_{0.5}K_{0.5})NbO_3$-0.04$(Ba_{(1-x)}Sr_x)TiO_3$ were 139 pC/N, 0.31 %, 95, 0.04 at the composition of x=0.04.