Poly(3,4-ethylenedioxythiophene) (PEDOT), which has the highest stability in conducting polymer was employed to electrochromic (EC) film and studied about electrochromic properties according to the film fabrication method. PEDOT films were coated by two different methods, electropolymerization (EP) and vapor phase polymerization (VPP). Both of PEDOT films showed dark blue color at dedoped neutral state. Spectroelectrochemistry, switching ability and stability of the devices were investigated by UV-Vis Spectrophotometer and Cyclic voltammetry. Surface morphologies of the PEDOT VPP film at oxidized and reduced state were obtained by AFM. The average surface roughness of the PEDOT-VPP film was 50 nm and more homogeneous than that of the PEDOT-EP. The EC property from the PEDOT-VPP film was improved compared to that of the PEDOT-EP film, to show a response time of 1.5 sec, transmittancechange of 49%, and coloration efficiency of 402.