We have studied on welding dissimilar materials of cold-reduced carbon steel sheet and stainless steel sheet together by using laser beam. It is well known that stainless steel is so strong againt rust and heat, while cold-reduced carbon steel is widely used in various parts of industry. In this research we have performed some experiments to know the possibility of welding dissimilar materials using laser beam by adjusting the power output of 3kW laser. Other conditions of the experiments were as follows : the welding speed was varied in the range between 2m/min and 7m/min, argon gas and helium gas were used as shield gas, the flow value of shield gas was ranged between $10{ell}/min$ and $30{ell}/min$, and the gap of two materials was ranged between 0mm and 0.3mm. In order to ascertain of the welded surface, we have done the tensile strength testing, the hardness testing and the microscope observation. As a result, we have found that tensile strength was the highest at the condition of the welding speed of 4, the flow value of $20{ell}/min$, the gap of two materials 0, and the use of helium gas. Above testings have also showed that the tensile strength was generally satisfactory since the penetration of welding was almost complete due to the thinness of the materials. In addition, the formation of the welded area was excellent when it had the highest tensile strength.