수열합성법을 이용하여 전구체 용액 농도에 따라 성장된 ZnO 나노막대의 특성에 대한 연구를 수행하였다. ZnO 씨앗층은 sol-gel법으로 코팅하였고, 그 위에 ZnO 나노막대는 전구체 용액 농도를 0.01 M에서 0.3 M로 변화하여 성장시켰다. FE-SEM (field-emission scanning electron microscopy), XRD (X-ray diffraction), PL (photoluminescence)을 사용하여 ZnO 나노막대의 특성 변화를 분석하였다. 전구체 용액의 농도가 증가함에 따라 ZnO 나노막대의 직경과 길이가 증가하였으며 광학적 특성이 향상되었다.
ZnO nanorods were grown on ZnO seed layer by hydrothermal method. The ZnO seed layer was coated by sol-gel method, and then the ZnO nanorods on ZnO seed layer were grown with different precursor concentrations ranging from 0.01 M to 0.3 M. FE-SEM (field-emission scanning electron microscopy), XRD (X-ray diffraction), and PL (photoluminescence) were employed to investigate the structural and optical properties of the ZnO nanorods. The diameter and length of ZnO nanorods are increased and also the optical properties are enhanced as the precursor concentrations are increased.