The effects of alloying elements on the mechanical properties of normalized and quenched 3.60wt%C-2.60wt%C ductile cast iron poured into shell stack mold were investigated. The strength and hardness of as-cast specimen were increased and the elongation of it was decreased with the additions of Mn, Cu and Sn. The strength and hardness were increased with the addition of 0.40wt%Mo and then rather decreased with the increased addition of 0.80wt%. The strength and hardness were increased with normalizing treatment and the strengths of normalized specimens were increased slightly with the addition of alloying elements except Mo. Meanwhile the yield strength of the normalized specimen was increased slightly with the addition of Mo, the tensile strength was not changed much. Meanwhile the hardness and strength of the quenched specimen were slightly increased with the addition of Mn, those were almost not changed with the amount added. The tensile strength of the quenched specimen with larger diameter, when the Cu had been added, and the tensile and yield strengths of them, when Mo had been added, were increased with the addition of alloying element. On the other hand, those were not changed with the amount added. For the case of specimen with smaller diameter, there were no effects of these two elements. When Sn had been added, the strength of hardened specimen with larger diameter was slightly increased with the amount added. However, that with smaller diameter was rather decreased with it. The effect of specimen diameter on the strength of quenched specimen with the addition of Cu, Mo and Sn was reduced.