The wall thinning phenomenon of pipes was simulated as metal loss due to erosion and corrosion. Such wall thinning defects in the pipes of power plants are a very important safety consideration. In this study, we analyzed wall thinning defects that occurred by weld bead of weld zone of boost pump recirculation pipe. From the results of the analysis of pipe failures, numerical analysis was performed by Fluent v6.3.26 using the standard k-$varepsilon$ model of the weld bead shape, such as an elliptical or a spherical shape, on the inner wall of the pipe. Using the results obtained, we showed the overlap effect by cavitations corrosion and erosion-corrosion at the bottom of the wall-thinning defect.