Electrical and structural properties were investigated on the effects of ZnO and the lead-free NKN-LST ceramics with the addition of ZnO were fabricated by a conventional mixed oxide method. A gradual change in the crystal and microstructure was observed with the increase of ZnO addition. For the NKN-LST-ZnO ceramics sintered at $1050^{circ}C$, bulk density increased with the addition of ZnO and showed maximum value at addition 2.0mol% of ZnO. Curie temperature of the NKN-LST-ZnO ceramics slightly decreased with adding ZnO. The dielectric constant, piezoelectric constant ($d_{33}$) and electromechanical coupling factor ($k_p$) increased at the small amount of ZnO addition, which might be due to the increase in density. The high piezoelectric properties = 153 pC/N, electromechanical coupling factor = 0.484 and dielectric constant = 2883 were obtained for the NKN-LST+0.5ZnO ceramics sintered at $1050^{circ}C$ for 2h.