Acoustic emission (AE) signal from an HTS tape has a low signal to noise ratio, due to the large amount of noise caused by the boiling of the liquid cryogen or mechanical vibration from the cryo-cooler. In an attempt to improve the sensitivity of the AE sensor, $Pb(Zr_{0.54}Ti_{0.46})O_3$ + 0.2 wt% $Cr_2O_3$ + 1.0 wt.% $Nb_2O_5$ ceramics sintered at $1200^{circ}C$ was synthesized. In addition, the resonance ($f_r$) and anti-resonance frequencies ($f_a$) were measured using the specimens with various thicknesses (1.0, 1.5, 2.0, 2.5 and 3.0 mm). According to the test results, large AE signals with high frequencies were obtained from the AE sensor fabricated using a piezoelectric disc with a thinner thickness.