We investigated the electrical properties the starting material and sintering condition on the laminated PTC thermistor for micro circuit protection. The influences of $BaTiO_3$ powder with the 0.3 and 0.45 ${mu}m$ size and the electrical characteristics (Ba,Sr)$TiO_3$ sintered at 1350~1400$^{circ}C$ for 2 h in a reducing atmosphere (1% $H_2/N_2$). The sintered (Ba,Sr)$TiO_3$ was increased pore and the grain size was decreased according to increasing Sr additions. In relative permittivity, the phase transition temperature of (Ba,Sr)$TiO_3$ was decreased for 2.5$^{circ}C$ according to increasing 0.01 mole Sr additions, and the phase transition dose not appeared about 0.3 mole Sr addition. The (Ba,Sr)$TiO_3$ was show the low resistance from 0.01 mole to 0.05 mole by Sr addition, regardless of sintering temperature. The (Ba,Sr)$TiO_3$ was show $10^2$ jump order at 0.1 and 0.2 mole Sr addition, and PTCR of the sintered $(Ba_{0.7}Sr_{0.3})TiO_3$ does not appeared about 0.3 mole Sr addition, regardless of the sintering temperature and starting material size.