The formation of oxide superconducting phase fabrication of superconducting wire materials and fabrication of precise superconducting material were studied for developing superconductor application technique. The $ZrO_2$ addition reduced the particle size $BaZrO_3$ trapped in the matrix after the sintering growth. The added $ZrO_2$ was converted to fine particles of $BaZrO_3$ which is the conventional sintering temperature for YBaCuO, $Y_2Ba_1Cu_1O_5$ and CuO are formed as by products of the reaction between $ZrO_2$ and YBaCuO phase. The formation of highly $BaZrO_3$ particle appears to be responsible for the refinement of $BaZrO_3$ phase after the citric acid sintering process.