In this study, non-stoichiometric 1-x$[(K_{0.5}Na_{0.5})_{0.97}(Nb_{0.96}Sb_{0.04})O_3]$ + x $CeMnO_3$ + 0.8 mol%CuO + 0.2 wt% $Ag_2O$ (x=0, 0.005) ceramics were prepared by a conventional mixed oxide and carbonate method, their dielectric and piezoelectric properties were investigated with the variations of sintering temperature. As $CeMnO_3$ substitution incereased, the density, piezoelectric constant($d_{33}$) and dielectric constant($varepsilon_r$) were increased and the mechanical quality factor(Qm) was decreased. At the sintering temperature of $1100^{circ}C$, the density, electromechanical coupling factor($k_p$), dielectric constant($varepsilon_r$) and piezoelectric constant($d_{33}$) of 0.5mol% $CeMnO_3$ specimen showed the optimun values of 4.475 $g/cm^2$, 0.437, 552 and 166 pC/N, respectively. However, the mechanical quality factor($Q_m$) showed the minimum value of 380.