In the present study, crack healing effect and residual stress of $Al_2O_3$ ceramics were investigated by changing the sintering temperature and heat treatment conditions. And also it was investigated that the influence of different filler loadings of nano-sized SiC particles on the crack healing behavior of $Al_2O_3$ ceramics. The test samples were characterized by three point bend flexural tests to evaluate their mechanical properties. The morphological changes were studied by FE-SEM and EDS. The test results indicated that the $Al_2O_3$ with nano-sized SiC ceramics sintered at $1800^{circ}C$ were showed highest density. Sintering temperature at $1800^{circ}C$, the bending strength of heat treatment in air atmosphere specimens showed about 42 % increment in comparison to the un-heat treated specimens. The cracked specimens can be healed by heat treatment in vacuum atmosphere but the crack healing effect of $Al_2O_3$ ceramics, which is heat treated in air atmosphere was higher than that of heat treated in vacuum atmosphere. $Al_2O_3$ with 30 wt% of SiC ceramics indicated higher crack healing ability than that with 15 wt% of SiC ceramics. The FE-SEM images showed that the median cracks and pores were disappeared after heat treatment in air.