Blends were prepared by mixing BR, SBR and NBR to CIIR, which is used for outsole, at various mixing ratio, and effect of the mixing ratio on abrasion resistance and coefficient of friction was analyzed. CIIR interferes the crystalline formation of BR in BR/CIIR blends and this could be one of the factors that rapidly decreases abrasion resistance of BR/CIIR blends. $Tan{delta}$ peak area of CIIR/BR blends decreased as the amount of BR present in the blends increased, and similarly, the coefficient of friction tended to decrease. Stress relaxation rate and rebound resilience of CIIR/BR blends decreased with increasing BR content, and it was presumed that their rebound resilience was affected by stress relaxation rate.