Al/SiC composites were fabricated by thermal spray process, and the dry sliding wear tests were performed using the various sliding speed of 10, 30, 60 and 90 RPM through 1000 cycles. The applied load was 10 N and radius of wear track was 15 mm. Wear tracks on the Al/SiC composites were investigated using scanning electron microscope(SEM) and energy dispersive X-ray spectroscopy (EDS). In the case of sliding speed of 10 RPM, adhesive wear behavior caused by plastic deformation of composits surface was observed. In the cases of sliding speed of 30, 60, 90 RPM, abrasive wear behavior on the adhered layer formed by debris were observed. Through this study, it was found that the wear behavior of Al/SiC composites was mainly influenced by the sliding speed.