Purpose: This study was investigated the bonding strength of two kinds of Ni-Cr alloy with respect to the condition of surface treatment. Methods: The surface treatment was performed on the two kinds of Ni-Cr alloy (B alloy and R alloy) specimens, which were sandblasted with $50{mu}m$, $110{mu}m$, and $250{mu}m$ aluminium oxide and were treated with opaque application (paste and wash opaque). The roughness on the surfaces of the specimens was observed. The metal-ceramic interfaces were analyzed with EPMA in order to ionic diffusion, and the shear test was performed. Results: The BA250 specimen, which has higher surface roughness, showed the highest bonding strength in B specimens. In R specimens, the bonding strength of RA110 specimen was the highest. Conclusion: B specimen formed a mechanical bond between metal-ceramic interfaces; however, in the case of R specimen, a chemical bond was formed between that interfaces. There was no significant statistical difference between the bonding strengths of two types of specimens (p>0.05).