A NiW functional alloy plating was investigated as variables of metal ion concentration, complexing agent, temperature, pH and applied current density. Even if numerous studies on reaction mechanism of NiW induced codeposition were carried out during couples of decade, it has not been acceptable reaction mechanism. This study was focused on the effect of the plating variables on the alloy composition in the NiW alloy plating. Applied current density could control mainly the alloy composition rather than other plating variables. It has also been confirmed that the functional alloy plating such as layered or gradient plating was possible by controlling applied current density.