Structural and electrochemical properties of spinel oxide $LiMn_2O_4$ thin films prepared by using a sol-gel method on Pt/Ti/$SiO_2$/Si substrates were investigated. When Li/Mn molar ratio of the film was smaller than 0.5, $Mn_2O_3$hase was found to coexist with $LiMn_2O_4$. Half-cell batteries fabricated using the $LiMn_2O_4$ films as the cathode were put into chargedischarge (C-D) cycles and the change in structural properties of the cathode after the cycles was examined by X-ray diffraction and Raman spectroscopy. As the C-D cycle number increases, the discharge capacity of pure $LiMn_2O_4$ battery gradually decreases, being reduced to 72% of the initial capacity at 300 cycles. Such capacity fading is attributable to the decrease in the number of $Li^+$ ions that return to the tetrahedral sites of the spinel structure during the discharge step and the resultant increase in $Mn^{4+}$ density in the film. Also, $Mn_2O_3$ phase gradually appeared in the film as the cycle number increases.