This research was performed to evaluate physical properties of polysulfide epoxy overlay material for bridge deck as part of a review for possibility of domestic application of polymer concrete for bridge deck pavement. In order to evaluate strength characteristics, compressive strength, flexural strength and bond strength were tested, and, for durability characteristics, chloride ion penetration resistance and freeze/thaw resistance were tested along with ultraviolet rays impact evaluation. The tests showed that the results met the criteria suggested by the American Concrete Institute in terms of compressive strength, flexural strength and bond strength. However, in terms of the strengths measured at various test temperatures, it was found that the epoxy material was highly dependent on temperature, and, therefore, this should be considered at the time of domestic application of the epoxy material later. Deflection characteristics was checked through flexural strength test and it was found that bridge deck pavement using the epoxy material was excellent compared to bridge deck pavement using asphalt. Furthermore, the results of chloride ion penetration resistance test and freeze/thaw resistance test were also excellent. In the evaluation of ultraviolet rays impact on epoxy slurry mixture, reduction of strain was noticed with increased strength, but the deflection characteristics after exposure to ultraviolet rays was better than the existing acryl polymer concrete. Therefore, it is concluded from the research that the polysulfide epoxy overlay material has the physical properties that are appropriate to pavement of bridge deck.