The behavior of abrasive wear on counterpart roughness of glass fiber reinforcement polyurethane resin (GF/PUR) composites were investigated at ambient temperature by pin-on-disc friction test. The friction coefficient, cumulative wear volume and surface roughness of these materials against SiC abrasive paper were determined experimentally. The major failure mechanisms were lapping layers, ploughing, delamination, deformation of resin and cracking by scanning electric microscopy (SEM) photograph of the tested surface. As increasing the counterpart roughness the GF/PUR composites indicated higher friction coefficient. The surface roughness of the GF/PUR composites was increased as the sliding velocity was higher and the counterpart roughness was rougher in wear test.